Adhesive property enhancement by photochemical modification on polyimide sheet surface by irradiation with excimer lamp
Book
·
OSTI ID:490888
- Tokai Univ., Hiratsuka, Kanagawa (Japan). Faculty of Engineering
Polyimide sheet surface was photochemically modified to be hydrophilic property with Xe{sub 2}* excimer lamp ({lambda} = 172 nm) irradiation and pure water solution. The solution was sandwiched between the surface and fused silica glass. With the excimer lamp irradiation, the solution and the surface were excited; the surface was dehydrogenated by the hydrogen atoms which were photodissociated from pure water and replaced the photodissociated OH radicals. The hydrophilic property of the modified surface was evaluated by measuring the contact angle with water. The replacement of the OH radicals were confirmed by FTIR. The modified surface was bonded to stainless steel with an epoxy resin for evaluation of the adhesive strength by the shearing tensile test. As a result, the adhesion was increased to 1.4 times that of the non-irradiated sample.
- OSTI ID:
- 490888
- Report Number(s):
- CONF-951155--; ISBN 1-55899-300-2
- Country of Publication:
- United States
- Language:
- English
Similar Records
Use of an excimer lamp for photochemical resistless etching of thermal silicon oxide substrate
High efficiency fluorescent excimer lamps: An alternative to mercury based UVC lamps
Charge formation in polyimide films under the action of low-frequency glow-discharge plasma
Book
·
Mon Dec 30 23:00:00 EST 1996
·
OSTI ID:490886
High efficiency fluorescent excimer lamps: An alternative to mercury based UVC lamps
Journal Article
·
Sat Dec 14 23:00:00 EST 2013
· Review of Scientific Instruments
·
OSTI ID:22251248
Charge formation in polyimide films under the action of low-frequency glow-discharge plasma
Journal Article
·
Sat Jul 01 00:00:00 EDT 1995
· High Energy Chemistry
·
OSTI ID:171694