FUEL-BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Seventh Quarterly Report, Covering April 1, 1961 to June 30, 1961
Technical Report
·
OSTI ID:4843149
Irradiation specimens (tensile and bend) were machined and shipped to Battelle. These specimens were unclad and clad. The core material was Al- coated, enriched U-bearing fiberglas with a loading of 10.53 plus or minus 0.2 g of U/sup 235/ per plate. They will be preirradiation examined, encapsulated, and then irradiated in the MTR. Plates containing Al-coated, U-bearing fiberglas core sections can be clad with two types of material, i.e., alclad 5154 or alclad fiberglas-reinforced Al. The alclad fiberglas-reinforced Al must overlap the core edges by at least 1/32-inch. Plates containing Al-coated depleted U-bearing fiberglas core sections were formed with a 5.50-inch radius. Alclad 5154 plates can be formed at room temperature. Alclad fiberglas-reinforced Al plates must be formed at 350 to 500F. (auth)
- Research Organization:
- Clevite Corp. Mechanical Research Div., Cleveland
- NSA Number:
- NSA-15-028746
- OSTI ID:
- 4843149
- Report Number(s):
- ORO-460
- Country of Publication:
- United States
- Language:
- English
Similar Records
FUEL BEARING FIBERGLAS IN ALUMINUM-BASE FUEL ELEMENTS. Final Report
FUEL-BEARING FIBERGLAS IN ALUMINUM-BASE FUEL ELEMENTS-SIXTH QUARTERLY REPORT, JANUARY 1, 1961 TO MARCH 31, 1961
FUEL-BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Eighth Quarterly Report, July 1, 1961 to September 30, 1961
Technical Report
·
Fri Jun 01 00:00:00 EDT 1962
·
OSTI ID:4748113
FUEL-BEARING FIBERGLAS IN ALUMINUM-BASE FUEL ELEMENTS-SIXTH QUARTERLY REPORT, JANUARY 1, 1961 TO MARCH 31, 1961
Technical Report
·
Mon May 01 00:00:00 EDT 1961
·
OSTI ID:4025700
FUEL-BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Eighth Quarterly Report, July 1, 1961 to September 30, 1961
Technical Report
·
Sun Oct 29 23:00:00 EST 1961
·
OSTI ID:4820965