FUEL-BEARING FIBERGLAS IN ALUMINUM-BASE FUEL ELEMENTS-SIXTH QUARTERLY REPORT, JANUARY 1, 1961 TO MARCH 31, 1961
Technical Report
·
OSTI ID:4025700
Depleted, aluminum-coated, uranium-bearing fiberglas was used as core material for processing experimental fuel plates. Cladding the plates with alclad 5154 or alclad fiberglas-reinforced aluminum resulted in uniform crackfree core sections. The test program to be conducted with enriched plates is described. The results of bending tests with various clad depleted plates are reported; cladding with high-strength aluminum alloys was found to increase the formability to the extent that an alclad 5154 plats could be bent up to 180 deg at 450 deg F without breaking. (D.L.C.)
- Research Organization:
- Clevite Corp. Mechanical Research Div., Cleveland
- NSA Number:
- NSA-15-024531
- OSTI ID:
- 4025700
- Report Number(s):
- ORO-417
- Country of Publication:
- United States
- Language:
- English
Similar Records
FUEL-BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Seventh Quarterly Report, Covering April 1, 1961 to June 30, 1961
FUEL BEARING FIBERGLAS IN ALUMINUM-BASE FUEL ELEMENTS. Final Report
FUEL-BEARING FIBERGLAS IN ALUMINUM-BASE FUEL ELEMENTS. Summary Report, May 4, 1960-October 31, 1960
Technical Report
·
Thu Jul 20 00:00:00 EDT 1961
·
OSTI ID:4843149
FUEL BEARING FIBERGLAS IN ALUMINUM-BASE FUEL ELEMENTS. Final Report
Technical Report
·
Fri Jun 01 00:00:00 EDT 1962
·
OSTI ID:4748113
FUEL-BEARING FIBERGLAS IN ALUMINUM-BASE FUEL ELEMENTS. Summary Report, May 4, 1960-October 31, 1960
Technical Report
·
Wed Nov 30 23:00:00 EST 1960
·
OSTI ID:4028114