INTERMEDIATE-TEMPERATURE OXIDATION OF BERYLLIDES. Quarterly Progress Report, September 1, 1961-March 1, 1962
Technical Report
·
OSTI ID:4829416
Oxidation characteristics of ZrBe/sub 13/, Zr/sub 2/Be/sub 17/, NbBe/sub 12/ and Nb/sub 2/Be/sub 17/ were studied at temperatures between 1200 and 2000 deg F. Accelerated attack was observed in this temperature range compared with the neighboring temperatures. Thick white oxide coatings were produced, and the reaction was sometimes accompanied by metallic disintegration. X-ray diffraction and metallography were used to study the products and manifestations of oxidation, and thermogravimetric curves are presented for ZrBe/sub 13/ and Nb/sub 2/Be/sub 17/. (auth)
- Research Organization:
- Denver. Univ. Denver Research Inst.
- NSA Number:
- NSA-16-024123
- OSTI ID:
- 4829416
- Report Number(s):
- TID-16030; DRI-2031
- Country of Publication:
- United States
- Language:
- English
Similar Records
INTERMEDIATE-TEMPERATURE OXIDATION OF BERYLLIDES. Quarterly Progress Report, June 1 to September 1, 1962
INTERMEDIATE-TEMPERATURE OXIDATION OF BERYLLIDES. Quarterly Progress Report, September 1 to December 1, 1962
INTERMEDIATE-TEMPERATURE OXIDATION OF BERYLLIDES. Monthly Letter Report No. 11, July 1, 1962-August 1, 1962
Technical Report
·
Sat Sep 15 00:00:00 EDT 1962
·
OSTI ID:4763568
INTERMEDIATE-TEMPERATURE OXIDATION OF BERYLLIDES. Quarterly Progress Report, September 1 to December 1, 1962
Technical Report
·
Sun Dec 09 23:00:00 EST 1962
·
OSTI ID:4734621
INTERMEDIATE-TEMPERATURE OXIDATION OF BERYLLIDES. Monthly Letter Report No. 11, July 1, 1962-August 1, 1962
Technical Report
·
Wed Aug 01 00:00:00 EDT 1962
·
OSTI ID:4783307