REPORT OF DRY RUNNING TWO 440-C HEAT TREATED STAINLESS STEEL ANNULAR BALL BEARINGS IN A HELIUM ATMOSPHERE AT 510 F TEMPERATURE
Technical Report
·
OSTI ID:4818823
The results of rotating a 440 deg C heat-treated air-melted stainless steel, full complement, annular ball bearing under 1l70 lb radial loading at low speed in a heliuim atmosphere at a temperature of 5l0 deg F are presented. The two test bearings were operated undcr load for l2l,400 revolutions at an average speed of 4 rpm. The test was terminated after the required time of 500 hr was attained. Photograpbs are presented which show the test bearings after removal from the machine. Data are presented in tables and graphs. (M.C.G.)
- Research Organization:
- Messinger Bearings, Inc., Philadelphia
- NSA Number:
- NSA-16-004546
- OSTI ID:
- 4818823
- Report Number(s):
- TID-14359
- Country of Publication:
- United States
- Language:
- English
Similar Records
REPORT OF DRY RUNNING TWO 440-C HEAT-TREATED STAINLESS STEEL ANNULAR BALL BEARINGS IN A HELIUM ATMOSPHERE AT 510 F TEMPERATURE
REPORT OF DRY RUNNING TWO 440C HEAT-TREATED STAINLESS STEEL ANNULAR BALL BEARINGS IN A HELIUM ATMOSPHERE
STATIC SODIUM TEST OF WESTINGHOUSE FLOW CONTROLLER BEARING
Technical Report
·
Fri Sep 01 00:00:00 EDT 1961
·
OSTI ID:4818824
REPORT OF DRY RUNNING TWO 440C HEAT-TREATED STAINLESS STEEL ANNULAR BALL BEARINGS IN A HELIUM ATMOSPHERE
Technical Report
·
Tue Feb 28 23:00:00 EST 1961
·
OSTI ID:4838687
STATIC SODIUM TEST OF WESTINGHOUSE FLOW CONTROLLER BEARING
Technical Report
·
Wed Nov 30 23:00:00 EST 1960
·
OSTI ID:4000341