EFFECTS OF ROLLING AND HEAT TREATMENT ON ANISOTROPIC IRRADIATION GROWTH OF URANIUM. Final Report-Metallurgy Program 6.1.15
An investigation was made to determine the effect of rolling temperature, roll pass design, amount of reduction, and heat treatment before and after rolling on the anisotropic growth rate of uranium under irradiation. The growth rate was found to increase with decreasing rolling temperature and with increasing reduction of area at 300 deg C. The rate of elongation was proportional to the amount of (0l0) component present or, where shortening occurred, to the amount of (l00) component. Oval-edgeoval roll passes resulted in somewhat higher irradiation growth rates than did round roll passes. Recrystallization after rolling effectively reduced the irradiation growth rate of uranium rolled at temperatures of 500 deg C and lower. Irradiation caused length shortening in uranium which was beta quenched after being round-rolled at temperatures of 400 deg C and above, and which was beta quenched after being oval- rolled at temperatures of 300 deg C and above. (auth)
- Research Organization:
- Argonne National Lab., Ill.
- DOE Contract Number:
- W-31-109-ENG-38
- NSA Number:
- NSA-16-004584
- OSTI ID:
- 4818529
- Report Number(s):
- ANL-6344
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-62
- Country of Publication:
- United States
- Language:
- English
Similar Records
PREFERRED ORIENTATION IN ROLLED AND IN RECRYSTALLIZED HIGH-PURITY URANIUM ROD. Final Report of Metallurgy Program.4.1.17
PRESSURIZED WATER REACTOR (PWR) PROJECT TECHNICAL PROGRESS REPORT FOR THE PERIOD OCTOBER 24, 1960 TO DECEMBER 23, 1960