THE EFFECTS OF $gamma$-IRRADIATION AND ROLLING ON THE TEARING PROPERTIES OF POLYETHYLENE
Journal Article
·
· Nippon Kikai Gakkai Rombunshu (Japan)
OSTI ID:4818305
Polyethylene samples of 2 mm thickness were gamma irradiated in water. The total dosage for the samples irradiated after the rolling treatraent was 1.5 x lO/sup 5/ r/hr, while the dosage for the saraples irradiated before the rolling was 1.2 x lO/sup 5/ r/hr. The tensile strength of the irradiated and rolled saraple increased with increasing dosage. A comparison of tearing strengths between the rolled samples and the rolled and irradiated samples was raade. (OID)
- Research Organization:
- Originating Research Org. not identified
- NSA Number:
- NSA-16-024259
- OSTI ID:
- 4818305
- Journal Information:
- Nippon Kikai Gakkai Rombunshu (Japan), Vol. Vol: 27; Other Information: Orig. Receipt Date: 31-DEC-62
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
$gamma$-RAY-INDUCED GRAFT COPOLYMERIZATION. V. THE GRAFT COPOLYMERIZATION OF METHACRYLIC ACID TO POLYETHYLENE BY A PRE-IRRADIATION TECHNIQUE
GAMMA-RAY-INDUCED GRAFT COPOLYMERIZATION. IV. GRAFT COPOLYMERIZATION OF METHACRYLIC ACID TO POLYETHYLENE BY THE MUTUAL GRAFT TECHNIQUE
$gamma$-IRRADIATION OF NATURAL RUBBER LATEX
Journal Article
·
Tue May 01 00:00:00 EDT 1962
· Kobunshi Kagaku (Japan) Changed to Kobunshi Ronbunshu
·
OSTI ID:4818305
GAMMA-RAY-INDUCED GRAFT COPOLYMERIZATION. IV. GRAFT COPOLYMERIZATION OF METHACRYLIC ACID TO POLYETHYLENE BY THE MUTUAL GRAFT TECHNIQUE
Journal Article
·
Sun Apr 01 00:00:00 EST 1962
· Kobunski Kagaku
·
OSTI ID:4818305
$gamma$-IRRADIATION OF NATURAL RUBBER LATEX
Journal Article
·
Wed Nov 01 00:00:00 EST 1961
· Kogyo Kagaku Zasshi (Japan) Merged with Nippon Kagaku Zasshi to form Nippon Kagaku Kaishi
·
OSTI ID:4818305