THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY SHEET. Interim Technical Engineering Report, July 31, 1961-December 31, 1961
Technical Report
·
OSTI ID:4802580
Two 8-inch D31 ingots were found to be uniform in structure and chemical composition both within an ingot and between ingots, with the exception of variable Ti content. Sheet processed from various locations in the two ingots is very uniform in properties at 0 to 2200 deg F. D3l was found to be readily forgeable with relatively simple techniques. Lahoratory programs to determine optimum processing sequences for both F48 and D31 are near completion. (auth)
- Research Organization:
- Crucible Steel Co. of America. Midland Research Lab., Penna.
- NSA Number:
- NSA-16-010470
- OSTI ID:
- 4802580
- Report Number(s):
- ASD-TR-7-784(VI)
- Country of Publication:
- United States
- Language:
- English
Similar Records
THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY SHEET. Interim Technical Engineering Report, March 15, 1961-July 31, 1961
THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY FORGINGS. Interim Technical Engineering Report, March 15, 1961-August 15, 1961
THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY SHEET. Interim Technical Engineering Report, January 1, 1962-September 30, 1962
Technical Report
·
Fri Sep 01 00:00:00 EDT 1961
·
OSTI ID:4837618
THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY FORGINGS. Interim Technical Engineering Report, March 15, 1961-August 15, 1961
Technical Report
·
Tue Aug 01 00:00:00 EDT 1961
·
OSTI ID:4841706
THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY SHEET. Interim Technical Engineering Report, January 1, 1962-September 30, 1962
Technical Report
·
Fri Nov 30 23:00:00 EST 1962
·
OSTI ID:4763144