INFLUENCE OF NEUTRON-IRRADIATION AT 78 K ON THE CRITICAL FIELD OF SUPERCONDUCTING LEAD
Measurements on the critical field of neutron-irradiated lead are given. Lead wires, soft-annealed for 2 hours at 200 un. Concent 85% C in vacuo, were encapsulated in an evacuated silica tube and subsequently irradiated in a low flux reactor for a period of eleven days at a temperature of 78 un. Concent 85% K. The integrated flux was about 10/sup 18/ fast neutrons cm/sup -2/. Values of the residual resistivity measured before irradiation and after recovery for 20 minutes at 353 un. Concent 85% K are listed. (C.E.S.)
- Research Organization:
- Philips' Gloeilampenfabrieken, Eindhoven, Netherlands
- NSA Number:
- NSA-17-020532
- OSTI ID:
- 4716528
- Journal Information:
- Phys. Letters, Journal Name: Phys. Letters Vol. Vol: 4
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
RESISTIVITY OF DOPED IRON IRRADIATED WITH FAST NEUTRONS AT 78 K
EXAMINATION OF THE CRYSTAL STRUCTURE OF ALPHA-PLUTONIUM AT LOW TEMPERATURE
A STUDY OF FERROELECTRIC MATERIALS. Final Technical Report, September 1, 1961 to August 31, 1962
Journal Article
·
Sun Mar 10 23:00:00 EST 1963
· Compt. Rend.
·
OSTI ID:4727055
EXAMINATION OF THE CRYSTAL STRUCTURE OF ALPHA-PLUTONIUM AT LOW TEMPERATURE
Journal Article
·
Thu Feb 28 23:00:00 EST 1963
· Cryogenics (England)
·
OSTI ID:4720981
A STUDY OF FERROELECTRIC MATERIALS. Final Technical Report, September 1, 1961 to August 31, 1962
Technical Report
·
Tue Sep 25 00:00:00 EDT 1962
·
OSTI ID:4712416