A HARDENING EFFECT ASSOCIATED WITH STAGE III RECOVERY IN NEUTRON IRRADIATED MOLYBDENUM
Polycrystalline tensile specimens of molybdenum of average grain diameter 75 mu were irradiated at approximates 40 deg C with an epithermal neutron dose of approximately 2 x 10/sup 18/ nvt. Specimens were annealed for one hour at temperatures of unirradiated specimens, irradiated and annealed specimens, and irradiated but unannealed specimens were tested at room temperature in a tensometer at a strain rate of 0.9 x 10/sup -4/ sec.sup -1/. The effect of the radiation was to increase the yield stress without significantly altering the rest of the load-elongation curve. (C.E.S.)
- Research Organization:
- Imperial Coll. of Science and Tech., London
- Sponsoring Organization:
- USDOE
- NSA Number:
- NSA-17-027922
- OSTI ID:
- 4687300
- Journal Information:
- Phil. Mag., Journal Name: Phil. Mag. Vol. Vol: (8), 8
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
Stage III recovery in neutron irradiated molybdenum and niobium
THE RELATIVE IMPORTANCE OF GRAIN BOUNDARIES AND SUB-GRAIN BOUNDARIES IN THE IRRADIATION HARDENING OF MOLYBDENUM
CRYSTALLINITY IN FUSED SILICA INDUCED BY FAST NEUTRON IRRADIATION
Journal Article
·
Sun Mar 31 23:00:00 EST 1963
· Philosophical Magazine
·
OSTI ID:4693297
THE RELATIVE IMPORTANCE OF GRAIN BOUNDARIES AND SUB-GRAIN BOUNDARIES IN THE IRRADIATION HARDENING OF MOLYBDENUM
Journal Article
·
Wed Aug 01 00:00:00 EDT 1962
· Phil. Mag.
·
OSTI ID:4769311
CRYSTALLINITY IN FUSED SILICA INDUCED BY FAST NEUTRON IRRADIATION
Journal Article
·
Tue Oct 01 00:00:00 EDT 1963
· Journal of Applied Physics (U.S.)
·
OSTI ID:4081063