CORROSION RESISTANCE OF NICKEL-BASE ALLOYS IN A NaF-LiF-ZrF$sub 4$ SALT MIXTURE CONSIDERED FOR EBR-1 FUEL RECOVERY
Technical Report
·
OSTI ID:4679294
The corrosive effects of NaF- LiF-- ZrF/sub 4/ (52-37-11 mole%), a suggested salt for EBR-1 fuel recovery, were investigated for the following Ni- base alloys: INOR-8, HyMu-80, Alloy 2 (85 Ni--10 Mo-5 Fe), ORNL 23 (Ni5 Fe), ORNL 3 (Ni-- 1 Al), and INCO 61. The run was conplease delete the above abstract----
- Research Organization:
- Battelle Memorial Inst., Columbus, Ohio
- DOE Contract Number:
- W-7405-ENG-92
- NSA Number:
- NSA-17-034345
- OSTI ID:
- 4679294
- Report Number(s):
- BMI-X-247
- Country of Publication:
- United States
- Language:
- English
Similar Records
CORROSION RESISTANCE OF NICKEL-BASE ALLOYS IN A NaF-LiF-BeF$sub 2$-ZrF$sub 4$- MIXTURE UNDER HYDROFLUORINATOR CONDITIONS AT 500 C, WITH AND WITHOUT ZIRCALOY-2 DISSOLVING. PART II
CORROSION RESISTANCE OF NICKEL-BASE ALLOYS UNDER HYDROFLUORINATOR CONDITIONS WITH ALUMINUM DISSOLVING. PART II
CORROSION RESISTANCE OF EXPERIMENTAL NICKEL-BASE ALLOYS UNDER HYDROFLUORINATOR CONDITIONS
Technical Report
·
Fri Aug 23 00:00:00 EDT 1963
·
OSTI ID:4651995
CORROSION RESISTANCE OF NICKEL-BASE ALLOYS UNDER HYDROFLUORINATOR CONDITIONS WITH ALUMINUM DISSOLVING. PART II
Technical Report
·
Fri Oct 18 00:00:00 EDT 1963
·
OSTI ID:4151127
CORROSION RESISTANCE OF EXPERIMENTAL NICKEL-BASE ALLOYS UNDER HYDROFLUORINATOR CONDITIONS
Technical Report
·
Fri Nov 30 23:00:00 EST 1962
·
OSTI ID:4735535