STUDY OF THE INTERNAL FRICTION PEAKS OBSERVED AFTER COLD-WORKING IN Ti AND Zr AT LOW TEMPERATURE. (in French)
Journal Article
·
· J. Phys. (Paris), Colloq. 71: No. 2, 215-20 (1971).
OSTI ID:4674736
- Research Organization:
- Ecole Nationale Superieure de Mecanique et d'Aerotechnique, Poitiers, France
- NSA Number:
- NSA-26-012630
- OSTI ID:
- 4674736
- Journal Information:
- J. Phys. (Paris), Colloq. 71: No. 2, 215-20 (1971)., Journal Name: J. Phys. (Paris), Colloq. 71: No. 2, 215-20 (1971).
- Country of Publication:
- France
- Language:
- French
Similar Records
LOW-TEMPERATURE INTERNAL-FRICTION PEAKS IN COLD-WORKED NIOBIUM
STUDY OF THE INTERNAL FRICTION PEAKS OBSERVED AFTER COLD-WORKING IN b.c.c. METALS (Nb, Mo).
INTERNAL FRICTION PEAKS IN COLD-WORKED METALS
Journal Article
·
Mon Jan 31 23:00:00 EST 1966
· J. Inst. Metals.
·
OSTI ID:4555909
STUDY OF THE INTERNAL FRICTION PEAKS OBSERVED AFTER COLD-WORKING IN b.c.c. METALS (Nb, Mo).
Journal Article
·
Thu Dec 31 23:00:00 EST 1970
· J. Phys. (Paris), Colloq. 71: No. 2, 221-8(1971).
·
OSTI ID:4700919
INTERNAL FRICTION PEAKS IN COLD-WORKED METALS
Journal Article
·
Sat Mar 31 23:00:00 EST 1962
· Acta Met.
·
OSTI ID:4791874
Related Subjects
AGING
ANNEALING
COLD WORKING
DEFORMATION
IMPURITIES
INTERNAL FRICTION
LOW TEMPERATURE
N30130* --Metals
Ceramics
& Other Materials--Metals & Alloys--Properties Evaluations
TITANIUM
TITANIUM/internal friction peaks in
effects of cold-working at -60 to 50$sup 0$C on
ZIRCONIUM
ZIRCONIUM/internal friction peaks in
effects of cold- working at -60 to 50$sup 0$C on
ANNEALING
COLD WORKING
DEFORMATION
IMPURITIES
INTERNAL FRICTION
LOW TEMPERATURE
N30130* --Metals
Ceramics
& Other Materials--Metals & Alloys--Properties Evaluations
TITANIUM
TITANIUM/internal friction peaks in
effects of cold-working at -60 to 50$sup 0$C on
ZIRCONIUM
ZIRCONIUM/internal friction peaks in
effects of cold- working at -60 to 50$sup 0$C on