ANNEALING FRIABILITY OF CONSTRUCTION STEEL WITH LANTHANUM ADMIXTURES (in Russian)
Journal Article
·
· Metalloved. i Term. Obrabotka Metal.
OSTI ID:4629553
Optimum friability annealing was reached with 0.15 to 0.23% La admixtures to KnLN steel and 0.26 to 0.30% La to 30KhGS steel. Admixtures of La are more effective than Mo in preventing intergrain disintegration. (R.V.J.)
- Research Organization:
- Ural Polytechnic Inst., USSR
- NSA Number:
- NSA-17-039578
- OSTI ID:
- 4629553
- Journal Information:
- Metalloved. i Term. Obrabotka Metal., Journal Name: Metalloved. i Term. Obrabotka Metal. Vol. Vol: No. 8
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
EFFECTS OF NIOBIUM ON THE TEMPERING FRIABILITY OF MANGANESE STEEL
THE AGING FRIABILITY OF 20XH14C2 STEEL AT 500 TO 650
THE INFLUENCE OF Cr AND Mn ALLOYING ON THE LOW-CARBON STEEL FRIABILITY
Journal Article
·
Sat Jan 31 23:00:00 EST 1959
· Metalloved. i Termich. Obrabotka Metal.
·
OSTI ID:4285050
THE AGING FRIABILITY OF 20XH14C2 STEEL AT 500 TO 650
Journal Article
·
Fri Aug 01 00:00:00 EDT 1958
· Metalloved. i Obrabotka Metal
·
OSTI ID:4302619
THE INFLUENCE OF Cr AND Mn ALLOYING ON THE LOW-CARBON STEEL FRIABILITY
Journal Article
·
Tue Sep 01 00:00:00 EDT 1959
· Metalloved. i Termichesk. Obrabotka Meta.
·
OSTI ID:4210476