EFFECTS OF NIOBIUM ON THE TEMPERING FRIABILITY OF MANGANESE STEEL (in Russian)
Journal Article
·
· Metalloved. i Termich. Obrabotka Metal.
OSTI ID:4285050
The annealing friability of manganese steel with various contents of niobium was tested in a highfrequency funnace in vacuum and in atmosphere. It was found that niobium sharply reduces the tendencies to friability. The optimum content of niobium is 0.25%. (R.V.J.)
- Research Organization:
- Khar'kov Polytechnic Inst.
- NSA Number:
- NSA-13-010093
- OSTI ID:
- 4285050
- Journal Information:
- Metalloved. i Termich. Obrabotka Metal., Journal Name: Metalloved. i Termich. Obrabotka Metal. Vol. Vol: No. 2
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
THE INFLUENCE OF Cr AND Mn ALLOYING ON THE LOW-CARBON STEEL FRIABILITY
ANNEALING FRIABILITY OF CONSTRUCTION STEEL WITH LANTHANUM ADMIXTURES
EFFECTS OF BORON ON THE TEMPER EMBRITTLEMENT OF CONSTRUCTION STEEL
Journal Article
·
Tue Sep 01 00:00:00 EDT 1959
· Metalloved. i Termichesk. Obrabotka Meta.
·
OSTI ID:4210476
ANNEALING FRIABILITY OF CONSTRUCTION STEEL WITH LANTHANUM ADMIXTURES
Journal Article
·
Thu Aug 01 00:00:00 EDT 1963
· Metalloved. i Term. Obrabotka Metal.
·
OSTI ID:4629553
EFFECTS OF BORON ON THE TEMPER EMBRITTLEMENT OF CONSTRUCTION STEEL
Journal Article
·
Fri May 01 00:00:00 EDT 1959
· Metalloved. i Termichesk. Obrabotka Metal.
·
OSTI ID:4205954