Development of twisted high-temperature superconductor composite conductors
- American Superconductor Corporation, Westborough, Massachusetts 01581 (United States)
Multifilamentary high-temperature superconductor (HTS) composite conductors have been developed for alternating current (ac) applications. A twisted HTS conductor containing the Bi-2223 phase fabricated using a modified powder-in-tube technique is reported. Transport critical current densities of 13 800 and 10 900 A/cm {sup 2} (77 K, self-field, 1 {mu}V/cm) have been achieved for twisted tape and wire conductors with twist pitches of 3.7 and 3.6 mm, respectively. These conductors are strongly linked and are thus suitable for use in ac applications.
- OSTI ID:
- 45952
- Journal Information:
- Applied Physics Letters, Vol. 66, Issue 17; Other Information: PBD: 24 Apr 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development of twisted high-temperature superconducting composites
ALTERNATING CURRENT LOSSES IN AG-SHEATHED BSCCO (2212 AND 2223) TAPES AND WIRES AND YBCO (123) COATED CONDUCTORS
Processing and characterization of Ag-clad Bi-2223 superconductors
Journal Article
·
Sun Jun 01 00:00:00 EDT 1997
· Advances in Cryogenic Engineering
·
OSTI ID:45952
ALTERNATING CURRENT LOSSES IN AG-SHEATHED BSCCO (2212 AND 2223) TAPES AND WIRES AND YBCO (123) COATED CONDUCTORS
Technical Report
·
Sat Jan 01 00:00:00 EST 2000
·
OSTI ID:45952
Processing and characterization of Ag-clad Bi-2223 superconductors
Conference
·
Thu Aug 01 00:00:00 EDT 1996
·
OSTI ID:45952
+5 more