ON RECRYSTALLIZATION IN ALUMINUM-COPPER ALLOYS (in French)
Journal Article
·
· Compt. rend.
OSTI ID:4334088
In Al-- Cu alloys, well laminated after dissolving and tempering, the lowering of the recrystallization temperature causes a passage from continuous growth to discontinuous growth of the grains from which appears precipitation. This fact, doubtless quite general, is the origin of certain heterogeneous textures. It should therefore be considered during recrystallization. (tr-auth)
- Research Organization:
- Originating Research Org. not identified
- NSA Number:
- NSA-12-005393
- OSTI ID:
- 4334088
- Journal Information:
- Compt. rend., Journal Name: Compt. rend. Vol. Vol: 246
- Country of Publication:
- Country unknown/Code not available
- Language:
- French
Similar Records
On the origin of the R orientation in the recrystallization textures of aluminum alloys
Effects of grain shape and texture on the yield strength anisotropy of Al-Li alloy sheet
DECORATION OF THE DISLOCATION LINES BY PRECIPITATES IN AN ALUMINUM-4% COPPER ALLOY AGED AT 250 C
Journal Article
·
Tue Jun 01 00:00:00 EDT 1999
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:677963
Effects of grain shape and texture on the yield strength anisotropy of Al-Li alloy sheet
Journal Article
·
Thu Feb 18 23:00:00 EST 1999
· Scripta Materialia
·
OSTI ID:335277
DECORATION OF THE DISLOCATION LINES BY PRECIPITATES IN AN ALUMINUM-4% COPPER ALLOY AGED AT 250 C
Journal Article
·
Wed Oct 01 00:00:00 EDT 1958
· Compt. rend.
·
OSTI ID:4331648