THE CONSTITUTION DIAGRAM OF COPPER TITANIUM ALLOYS (in Russian)
Journal Article
·
· Izvest. Akad. Nauk S.S.S.R. Otdel. Tekh. Nauk
OSTI ID:4331572
The presence of the eutectic transition L at 200 deg C an alpha + BETA at the temperature 870 plus or minus 1 d C was determined by thermal analysis and zone recrystallization. The composition at the eutectic point is 17.1% Ti. The diffusion of titanium in copper determined by the microhardness method showed the maximum diffusion at the eutectic temperature was 7.4% Ti. The microhardness was found to be 370 plus or minus 15 kg/mm/sup 2/. The constitution diagram for Cu--Ti up to 20% Ti is included. (R.V.J.)
- Research Organization:
- Originating Research Org. not identified
- NSA Number:
- NSA-12-013961
- OSTI ID:
- 4331572
- Journal Information:
- Izvest. Akad. Nauk S.S.S.R. Otdel. Tekh. Nauk, Journal Name: Izvest. Akad. Nauk S.S.S.R. Otdel. Tekh. Nauk Vol. Vol: No. 2
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
CONSTITUTION DIAGRAM OF TITANIUM-SCANDIUM ALLOYS
CONSTITUTION DIAGRAM OF TITANIUM-PALLADIUM ALLOY
NEW DATA ON In-Se CONSTITUTION DIAGRAM
Journal Article
·
Mon May 01 00:00:00 EDT 1961
· Zhur. Neorg. Khim.
·
OSTI ID:4843535
CONSTITUTION DIAGRAM OF TITANIUM-PALLADIUM ALLOY
Journal Article
·
Mon Oct 31 23:00:00 EST 1960
· Zhur. Neorg. Khim.
·
OSTI ID:4078948
NEW DATA ON In-Se CONSTITUTION DIAGRAM
Journal Article
·
Wed May 01 00:00:00 EDT 1963
· Zh. Neorgan. Khim
·
OSTI ID:4662262