PREFERRED ORIENTATION OF COLD-ROLLED AND RECRYSTALLIZED URANIUM PLATE
Technical Report
·
OSTI ID:4329894
The preferred orientation induced in uranium plate by mild cold rolling after beta transformation was characterized by measurement of thermal expansion coefficients. From these data, it was estimated that cold reductions of five and ten% would cause elongations of one and two% per 1000 Mwd/T, respectively, during irradiation of the plate. Recrystallization following cold work did not significantly affect the preferred orientation, but relieved intergranular stresses in the metal. The cold work and recrystallization reduced the grain size of the metal. (auth)
- Research Organization:
- Du Pont de Nemours (E.I.) & Co. Savannah River Lab., Augusta, Ga.
- DOE Contract Number:
- AT(07-2)-1
- NSA Number:
- NSA-12-012088
- OSTI ID:
- 4329894
- Report Number(s):
- DP-258
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-58
- Country of Publication:
- United States
- Language:
- English
Similar Records
PREFERRED ORIENTATION IN ROLLED AND IN RECRYSTALLIZED HIGH-PURITY URANIUM ROD. Final Report of Metallurgy Program.4.1.17
EFFECT OF HOT PRESS CLADDING ON MECHANICAL PROPERTIES AND MICROSTRUCTURE OF URANIUM PLATE
RECRYSTALLIZATION IN ROLLED URANIUM SHEET. Final Report--Metallurgy Program 4.1.5
Technical Report
·
Wed Apr 01 00:00:00 EST 1959
·
OSTI ID:4329894
EFFECT OF HOT PRESS CLADDING ON MECHANICAL PROPERTIES AND MICROSTRUCTURE OF URANIUM PLATE
Technical Report
·
Thu Dec 30 00:00:00 EST 1954
·
OSTI ID:4329894
RECRYSTALLIZATION IN ROLLED URANIUM SHEET. Final Report--Metallurgy Program 4.1.5
Technical Report
·
Thu Mar 01 00:00:00 EST 1962
·
OSTI ID:4329894