CHROMIUM PLATING FOR PROTECTION AGAINST STRESS CORROSION CRACKING OF HARDENED AISI 410 STEEL
Technical Report
·
OSTI ID:4329675
Because of its high corrosion resistance properties, chromium electroplate should offer protection to AISI 419 steel against stress corrosion cracking. Tests have been made (KAPL and Bettis) on chromium plates on test specimens as deposited by two different sources in conformance with Bettis and USMC specifications. These deposits either offered protection to hardened (RC36- 42) AISI 410 against stress corrosion cracking, or caused accelerated stress corrosion cracking under conditions which did not crack unplated material. At present there is no significant data which could give definite clues for these extreme differences in the corrosive protective values. The results of tests so far strongly question tbe value of chromium plate as a means to protect AISI 410 against stress corrosion cracking. (A.C.)
- Research Organization:
- Knolls Atomic Power Lab., Schenectady, N.Y.
- DOE Contract Number:
- W-31-109-ENG-52
- NSA Number:
- NSA-12-009146
- OSTI ID:
- 4329675
- Report Number(s):
- KAPL-M-HOS-4
- Country of Publication:
- United States
- Language:
- English
Similar Records
CHROMIUM ELECTROPLATES FOR CORROSION PROTECTION OF STRESSED AISI 410 IN HIGH TEMPERATURE, HIGH PURITY WATER
A DISCUSSION OF THE SUSCEPTIBILITY OF AISI 410 TO STRESS CORROSION, AND MEANS OF ELIMINATING THE STRESS-CORROSION PROBLEM
CHROMIUM ELECTROPLATES FOR CORROSION PROTECTION OF STRESSED AISI 410 STEEL IN HIGH TEMPERATURE, HIGH PURITY WATER
Technical Report
·
Tue Sep 01 00:00:00 EDT 1959
·
OSTI ID:4213498
A DISCUSSION OF THE SUSCEPTIBILITY OF AISI 410 TO STRESS CORROSION, AND MEANS OF ELIMINATING THE STRESS-CORROSION PROBLEM
Technical Report
·
Thu Mar 09 23:00:00 EST 1961
·
OSTI ID:4840127
CHROMIUM ELECTROPLATES FOR CORROSION PROTECTION OF STRESSED AISI 410 STEEL IN HIGH TEMPERATURE, HIGH PURITY WATER
Journal Article
·
Sat Oct 01 00:00:00 EDT 1960
· Corrosion
·
OSTI ID:4124248