CHROMIUM ELECTROPLATES FOR CORROSION PROTECTION OF STRESSED AISI 410 IN HIGH TEMPERATURE, HIGH PURITY WATER
Technical Report
·
OSTI ID:4213498
The use of chromium plates for protection of AISI 410 against stress corrosion cracking has given anomalous results. The coating either offered protection under conditions which produced failure in unplated material or caused accelerated failures under conditions in which unplated material did not fail. Factors which may have contributed to the anomalous results are discussed. Introduction of oxygen into rosion failures, especially for the chromium-plated samples, with applied stresses as low as 60,000 psi. From present available information, chromium deposits are not recommended for corrosion protection of AISI 410 materials susceptible to stress corrosion and/or intergranular attack.(auth)
- Research Organization:
- Knolls Atomic Power Lab., Schenectady, N.Y.
- DOE Contract Number:
- W-31-109-ENG-52
- NSA Number:
- NSA-13-022396
- OSTI ID:
- 4213498
- Report Number(s):
- KAPL-M-HOS-8
- Country of Publication:
- United States
- Language:
- English
Similar Records
CHROMIUM ELECTROPLATES FOR CORROSION PROTECTION OF STRESSED AISI 410 STEEL IN HIGH TEMPERATURE, HIGH PURITY WATER
A DISCUSSION OF THE SUSCEPTIBILITY OF AISI 410 TO STRESS CORROSION, AND MEANS OF ELIMINATING THE STRESS-CORROSION PROBLEM
CHROMIUM PLATING FOR PROTECTION AGAINST STRESS CORROSION CRACKING OF HARDENED AISI 410 STEEL
Journal Article
·
Sat Oct 01 00:00:00 EDT 1960
· Corrosion
·
OSTI ID:4124248
A DISCUSSION OF THE SUSCEPTIBILITY OF AISI 410 TO STRESS CORROSION, AND MEANS OF ELIMINATING THE STRESS-CORROSION PROBLEM
Technical Report
·
Thu Mar 09 23:00:00 EST 1961
·
OSTI ID:4840127
CHROMIUM PLATING FOR PROTECTION AGAINST STRESS CORROSION CRACKING OF HARDENED AISI 410 STEEL
Technical Report
·
Mon Apr 21 23:00:00 EST 1958
·
OSTI ID:4329675