THE ARC WELDING OF WROUGHT MAGNESIUM-THORIUM ALLOYS
Journal Article
·
· Welding J. (N.Y.)
OSTI ID:4306267
Results of welding evaluation tests on the recently developed, wrought, magnesium-base, thorium-coataining alloys are presented. These alloys possessed excellent weldability and retained high strengths at elevated temperatures after welding. The strengths of the welds were equal to, or closely approached, the strengths of the base metals at elevated temperatures. The creep resistance of the alloys was nct adversely affected by welding. Postweld heat treatments did not improve the weld strength to any marked degree. The corrosion rates in 3% NaCl solution were not changed significantly by welding. (auth)
- Research Organization:
- Dow Chemical Co., Midland, Mich.
- NSA Number:
- NSA-12-010660
- OSTI ID:
- 4306267
- Journal Information:
- Welding J. (N.Y.), Journal Name: Welding J. (N.Y.) Vol. Vol: 37
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
DEVELOPMENT OF WROUGHT ALUMINUM-MAGNESIUM ALLOYS. Technical Paper No. 14
Tensile-compressive yield asymmetries in high strength wrought magnesium alloys
Application of neutron diffraction in characterization of texture evolution during high-temperature creep in magnesium alloys
Technical Report
·
Tue Dec 31 23:00:00 EST 1957
·
OSTI ID:4252655
Tensile-compressive yield asymmetries in high strength wrought magnesium alloys
Journal Article
·
Fri Jul 15 00:00:00 EDT 1994
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:7108756
Application of neutron diffraction in characterization of texture evolution during high-temperature creep in magnesium alloys
Journal Article
·
Thu Dec 31 23:00:00 EST 2009
·
OSTI ID:986888