CREEP OF MAGNESIUM ALLOY AZ80-T5 AT LOW TEMPERATURES
Technical Report
·
OSTI ID:4302993
Magnesium alloy AZ80 (Wg-8.5 Al-1.0 Zn-0.25 Mn) in the T5 or age hardened condition was creep tested at 50 deg C and at various stresses. Creep rates were measured at the termination of tests which lasted from 600 to 1000 hrs. Extrapolation of the results show that a creep rate of 10/sup -5/%/hr is obtained at a stress of 10,000 psi. (auth)
- Research Organization:
- Atomic Energy of Canada Ltd. Chalk River Project, Chalk River, Ont.
- NSA Number:
- NSA-13-000751
- OSTI ID:
- 4302993
- Report Number(s):
- CRMet-794; AECL-689
- Country of Publication:
- Canada
- Language:
- English
Similar Records
CREEP AND TENSILE PROPERTIES OF MAGNESIUM ALLOY AZ61 AT 50 C
Creep of zirconium in water from 400 degree to 600 degree F
THE CREEP BEHAVIOUR OF THE MAGNESIUM-ZIRCONIUM ALLOY ZA AT 400 AND 450 C IN CARBON DIOXIDE CONTAINING /approximately equals/200 PPM MOISTURE
Technical Report
·
Sun Nov 30 23:00:00 EST 1958
·
OSTI ID:4265796
Creep of zirconium in water from 400 degree to 600 degree F
Technical Report
·
Thu Apr 19 23:00:00 EST 1951
·
OSTI ID:481274
THE CREEP BEHAVIOUR OF THE MAGNESIUM-ZIRCONIUM ALLOY ZA AT 400 AND 450 C IN CARBON DIOXIDE CONTAINING /approximately equals/200 PPM MOISTURE
Journal Article
·
Thu Feb 28 23:00:00 EST 1963
· Journal of Nuclear Materials (Netherlands)
·
OSTI ID:4687408