ROLLING AND ANNEALING TEXTURES OF BERYLLIUM AND HAFNIUM SHEET
Journal Article
·
· Trans. Met. Soc. AIME
OSTI ID:4284553
Beryllium dheet, cold rolled from 0.036 to 0.006 in., a reduction of 84%, exhibited a split texture with the STA1010! direction in the rolling direction. The same specimen annealed in vacuo for 1 hr at 1000 C showed no change in orientation. The deformation texture of 70% cold-rolled hafnium was similar to that of beryllium although the tilt about the rolling direction of about 15 was less. Hafuium sheet annealed in vacuo for 1 hr at 800 C or for 1 hr at 1000 C showed pole concentrations no longer in the rolling direction. (J.E.D.)
- Research Organization:
- General Electric Co., Schenectady, New York
- NSA Number:
- NSA-13-003897
- OSTI ID:
- 4284553
- Journal Information:
- Trans. Met. Soc. AIME, Journal Name: Trans. Met. Soc. AIME Vol. Vol: 212
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
THE ROLLING AND RECRYSTALLIZATION TEXTURE OF HAFNIUM
Investigation of the annealing texture evolution in hafnium
ON THE ROLLING AND RECRYSTALLIZATION TEXTURES OF ZIRCONIUM
Journal Article
·
Mon Jun 01 00:00:00 EDT 1959
· Z. Metallk.
·
OSTI ID:4220187
Investigation of the annealing texture evolution in hafnium
Journal Article
·
Sat Feb 28 23:00:00 EST 1998
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:616431
ON THE ROLLING AND RECRYSTALLIZATION TEXTURES OF ZIRCONIUM
Journal Article
·
Thu Nov 30 23:00:00 EST 1961
· Compt. rend.
·
OSTI ID:4803676