STRUCTURAL CHANGES IN SOLID SOLUTIONS OF TITANIUM AND NICKEL AT HIGH TEMPERATURES (in Russian)
Journal Article
·
· Fiz. Metal. i Metalloved.
OSTI ID:4274932
The effects of slow plastic deformation on the microstructure and recrystallization of solid solutions of nickel with 3.6% Ti (annealed for 2 to 3 hours at 1200 deg C) were investigated in vacuum at 700 to 900 deg C. (R.V.J.)
- Research Organization:
- Central Scientific Research Inst. of Ferrous Metals
- NSA Number:
- NSA-13-007807
- OSTI ID:
- 4274932
- Journal Information:
- Fiz. Metal. i Metalloved., Journal Name: Fiz. Metal. i Metalloved. Vol. Vol: 6
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
STRUCTURAL CHANGES OF Ni AND Ti SOLID SOLUTIONS IN Ni AT HIGH DEFORMATION TEMPERATURES
TRUE TEMPERATURE OF SATURATED SOLID SOLUTION INITIAL RECRYSTALLIZATIONS
THE STRENGTH OF NICKEL AT ROOM TEMPERATURE AND AT HIGH TEMPERATURES AS AFFECTED BY THE PARTICULAR STRUCTURAL STATE WHICH OCCURS DURING A HIGH-TEMPERATURE THERMO-MECHANICAL TREATMENT
Journal Article
·
Fri May 01 00:00:00 EDT 1959
· Fiz. Metal. i Metalloved. Akad. Nauk S.S.S.R., Ural Filial
·
OSTI ID:4198822
TRUE TEMPERATURE OF SATURATED SOLID SOLUTION INITIAL RECRYSTALLIZATIONS
Journal Article
·
Fri May 01 00:00:00 EDT 1959
· Izvest. Akad. Nauk S.S.S.R., Ser. Fiz.
·
OSTI ID:4205959
THE STRENGTH OF NICKEL AT ROOM TEMPERATURE AND AT HIGH TEMPERATURES AS AFFECTED BY THE PARTICULAR STRUCTURAL STATE WHICH OCCURS DURING A HIGH-TEMPERATURE THERMO-MECHANICAL TREATMENT
Journal Article
·
Fri Jun 01 00:00:00 EDT 1962
· Doklady Akad. Nauk S.S.S.R.
·
OSTI ID:4767616