THE CONSTITUTION DIAGRAM OF Ti-V-Nb ALLOY (in Russian)
Journal Article
·
· Zhur. Neorg. Khim.
OSTI ID:4226099
The constitution diagram and phase transformations of titanium-- vanadium- niobium solid solutions were investigated. The beta , alpha , and alpha + beta phase regions and their boundaries were found. The beta solid solution becomes continuous at >885 deg C, while below this temperature a limited solid solution is formed with a titanium a base modification. An alpha + beta region appears between the alpha and beta solid solutions. (R.V.J.)
- Research Organization:
- Originating Research Org. not identified
- NSA Number:
- NSA-13-020264
- OSTI ID:
- 4226099
- Journal Information:
- Zhur. Neorg. Khim., Journal Name: Zhur. Neorg. Khim. Vol. Vol: 4
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
CONSTITUTION DIAGRAM OF TITANIUM-SCANDIUM ALLOYS
CONSTITUTION DIAGRAM FOR PRASEO-DYMIUM-NEODYMIUM ALLOYS
POLYMORPHOUS TRANSFORMATIONS OF CHROMIUM AND CONSTITUTION DIAGRAM OF CHROMIUM RICH Cr-Ni ALLOYS
Journal Article
·
Mon May 01 00:00:00 EDT 1961
· Zhur. Neorg. Khim.
·
OSTI ID:4843535
CONSTITUTION DIAGRAM FOR PRASEO-DYMIUM-NEODYMIUM ALLOYS
Journal Article
·
Thu Aug 01 00:00:00 EDT 1963
· Zhur. Neorgan. Khim.
·
OSTI ID:4142503
POLYMORPHOUS TRANSFORMATIONS OF CHROMIUM AND CONSTITUTION DIAGRAM OF CHROMIUM RICH Cr-Ni ALLOYS
Journal Article
·
Mon May 01 00:00:00 EDT 1961
· Zhur. Neorg. Khim.
·
OSTI ID:4843536