RECRYSTALLIZATION OF DEFORMED ALPHA-URANIUM SINGLE CRYSTALS. Final Report- -Metallurgy Division Program 4.1.19. Work Completed-January 1, 1956
The orientation relationships between deformed alpha-uranium single crystals and recrystallized grains grown in them by annealing can be expressed as 27.5 deg rotations about axes located 70.0 deg from the STA100!, 63.5 deg from the STA010! and 34.0 deg from the STA001! of the deformed orientation. The rotations are clockwise about two of the axes and counterclockwise about the other two. In deriving these relationships it was necessary to consider the recrystallized grains as originating from deformation twin orientations as well as from the parent crystal orientation. The relationship agrees well with expermentel observations of recrystallization textures developed from deformation textures for polycrystalline rod and sheet uranium treated in the alpha phase. (auth)
- Research Organization:
- Argonne National Lab., Lemont, Ill.
- DOE Contract Number:
- W-31109-ENG-38
- NSA Number:
- NSA-13-020139
- OSTI ID:
- 4218384
- Report Number(s):
- ANL-6001
- Country of Publication:
- United States
- Language:
- English
Similar Records
RECRYSTALLIZATION OF DEFORMED ALPHA-URANIUM SINGLE CRYSTALS
DIMENSIONAL INSTABILITY OF URANIUM--IV. Final Progress Report for July 1, 1958-March 31, 1959
SECONDARY RECRYSTALLIZATION AND RECRYSTALLIZATION AFTER CRITICAL COLD WORKING OF HIGH PURITY URANIUM
Journal Article
·
Wed Jun 01 00:00:00 EDT 1960
· J. nuclear Materials
·
OSTI ID:4829579
DIMENSIONAL INSTABILITY OF URANIUM--IV. Final Progress Report for July 1, 1958-March 31, 1959
Technical Report
·
Sun Jan 31 23:00:00 EST 1960
·
OSTI ID:4168028
SECONDARY RECRYSTALLIZATION AND RECRYSTALLIZATION AFTER CRITICAL COLD WORKING OF HIGH PURITY URANIUM
Journal Article
·
Sun Sep 01 00:00:00 EDT 1963
· Journal of Nuclear Materials (Netherlands)
·
OSTI ID:4624600