X-RAY STUDIES OF THE INTERBOUND PROCESSES OF CONVERSION, RECRYSTALLIZATION AND ORDERING IN Fe-Co AND Ni-Fe ALLOYS

Journal Article · Fri May 01 04:00:00 EDT 1959 · Izvest. Akad. Nauk S.S.S.R., Ser. Fiz.

OSTI ID:4217626

Borodkina, M M; Detlaf, E I; Selisskii, Ya P

The results are given of x-ray studies made under intermittent temperature conditions of conversion in Fe--Co alloys and of the initial recrystallization stages in Fe--Co and Ni--Fe alloys. X-ray pictures are shown of the cold deformed Fe--Co with 42% Co taken at 650 to 800 deg C and Ni--Fe with 65, 70, 75, 8O, and 100% Ni after thermal treatment at 350 to 570 deg C. (R.V.J.) Measurements were made of the changes taking place in Nichrome (Al--0.76, C-- 0.045, Cr--21.1, Fe--0.32, Mn--0.33, Si--0.58, Ti--2.47 wt.%, remainder nickel) during annealing at 1080 deg C for 8 hours and at 1250 deg C for 16 hours. (R.V.J.) Studies were made of the changes taking place in the matrix of saturated metallic solid solutions of Ni--Be (1.9% Be) after annealing and high-temperature tempering. An anomalous diffractional, two-dimensional effect was observed in x- ray diffraction analysis after annealing at 425 to 500 deg C for 15 min. With increased annealing time the intensity of the effect rapidly increased. (R.V.J.)

• Research Organization: Baikov Inst. of Metallurgy, Academy of Sciences, U.S.S.R.
• NSA Number: NSA-13-020225
• OSTI ID: 4217626
• Journal Information: Izvest. Akad. Nauk S.S.S.R., Ser. Fiz., Journal Name: Izvest. Akad. Nauk S.S.S.R., Ser. Fiz. Vol. Vol: 23
• Country of Publication: Country unknown/Code not available
• Language: Russian

Related Subjects

COBALT ALLOYS
COLD WORKING
CRYSTALS
DEFORMATION
DISTRIBUTION
HEAT TREATMENTS
HIGH TEMPERATURE
IRON ALLOYS
METALLURGY AND CERAMICS
NICKEL ALLOYS
RECRYSTALLIZATION
X RADIATION