CONSTITUTION DIAGRAMS OF Fe-Cr-Ti AT IRON AND CHROMIUM RICH SIDE OF THE ALLOY

Journal Article · Fri Jan 01 04:00:00 EST 1960 · Izvest. Akad. Nauk S.S.S.R., Otdel. Tekh. Nauk, Met. i Toplivo

OSTI ID:4189446

Boriskina, N G; Kornilov, I I

ABS>Microstructure studies and x-ray-diffraction analysis were made of the Fe--Cr--Ti constitution diagram, and hardness was tested at 1000 and 550 deg C. Eutectic crystallization was observed in the Ti-- Fe region at the TiFe/sub 2/- -Cr cross section of the alloy, and a wide range of alloys was distributed in the right side with higher chromium content. The solubility of Ti in alpha solid solution increases in the Ti-Fe side at 1000 deg C and decreases at 550 deg C. The maximum hardness was found in tempered X phase alloys. (R.V.J.)

• Research Organization: Originating Research Org. not identified
• NSA Number: NSA-14-014079
• OSTI ID: 4189446
• Journal Information: Izvest. Akad. Nauk S.S.S.R., Otdel. Tekh. Nauk, Met. i Toplivo, Journal Name: Izvest. Akad. Nauk S.S.S.R., Otdel. Tekh. Nauk, Met. i Toplivo Vol. Vol: No. 1
• Country of Publication: Country unknown/Code not available
• Language: Russian

Related Subjects

CHROMIUM ALLOYS
CRYSTALLIZATION
DIFFRACTION
DISTRIBUTION
EUTECTICS
HARDNESS
HIGH TEMPERATURE
INTERMETALLIC COMPOUNDS
IRON ALLOYS
MATERIALS TESTING
METALLOGRAPHY
METALS, CERAMICS, AND OTHER MATERIALS
PHASE DIAGRAMS
SOLID SOLUTIONS
SOLUBILITY
TEMPERING
TITANIUM ALLOYS
X RADIATION