FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 11 for April 1, 1960 to April 30, 1960
Technical Report
·
OSTI ID:4180647
Fabrication techniques designed to eliminate the ripple effect produced in clad plates containing uranium-bearing fiberglas-core sections were investigated. The variables contributing to the rippled appearance are: edges of the pressed compacts, temperature of open and clad rolling and reduction ratio. The reduction in area of clad tensile specimens taken transverse to the rolling direction varied from 36 to 55% from room temperatare to 1000 deg F. (See also ORO-247). (C.J.G.)
- Research Organization:
- Clevite Corp. Mechanical Research Div., Cleveland
- NSA Number:
- NSA-14-016980
- OSTI ID:
- 4180647
- Report Number(s):
- ORO-277
- Country of Publication:
- United States
- Language:
- English
Similar Records
FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 15 for August 1, 1960 to August 31, 1960
FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 16 for Period September 1, 1960-September 30, 1960
FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 10 for March 1, 1960 to March 31, 1960
Technical Report
·
Mon Sep 12 00:00:00 EDT 1960
·
OSTI ID:4127094
FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 16 for Period September 1, 1960-September 30, 1960
Technical Report
·
Wed Oct 12 00:00:00 EDT 1960
·
OSTI ID:4115708
FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 10 for March 1, 1960 to March 31, 1960
Technical Report
·
Wed Apr 13 23:00:00 EST 1960
·
OSTI ID:4157831