FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 10 for March 1, 1960 to March 31, 1960
Technical Report
·
OSTI ID:4157831
In development of aluminum-coated fuel-bearing fiberglas core material twelve compacts were hot pressed during the report period. Techniques which affect core edges received particular attention. Four uranium-bearing fiberglas compacts were clad rolled during March. Some improvement over previously rolled core section was evidert; however, further wo.rk is required to produce plates which meet specifications. Tensile specimens taken transverse to the rolling direction were tested at room temperature, 250, 400, 600, and 800 deg F. The majority of the unclad transverse specimens displayed a greater strength at all temperatures than the specimens taken longitudinally to the rolling direction. (For preceding period see ORO-278.) (J.R.D.)
- Research Organization:
- Clevite Corp. Mechanical Research Div., Cleveland
- NSA Number:
- NSA-14-018144
- OSTI ID:
- 4157831
- Report Number(s):
- ORO-274
- Country of Publication:
- United States
- Language:
- English
Similar Records
FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 15 for August 1, 1960 to August 31, 1960
FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 11 for April 1, 1960 to April 30, 1960
FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 14, for Period July 1, 1960 to July 31, 1960
Technical Report
·
Mon Sep 12 00:00:00 EDT 1960
·
OSTI ID:4127094
FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 11 for April 1, 1960 to April 30, 1960
Technical Report
·
Tue May 10 00:00:00 EDT 1960
·
OSTI ID:4180647
FUEL BEARING FIBERGLAS IN ALUMINUM BASE FUEL ELEMENTS. Monthly Progress Letter No. 14, for Period July 1, 1960 to July 31, 1960
Technical Report
·
Tue Aug 16 00:00:00 EDT 1960
·
OSTI ID:4141937