TEXTURE DEFORMATION AND RECRYSTALLIZATION OF Fe-Ni (48% Ni) IN COLD ROLLING (in Russian)
Journal Article
·
· Fiz. Metal. i Metalloved.
OSTI ID:4171308
X-ray studies of thin (50 to 5 mu ) cold-rolled strips of Fe-- Ni (48%) show that the maximum deformation intensity is reached at approximately 99.0% orientation at (110) STA11-bar2! + (110) STA33-bar5, with clear-cut cubic recrystallization (110) STA001! texture observed after annealing. An increased deformation leads to transitions from (110) STA1-bar12! + (110) STA33-bar5! orientations to (112)STA111-bar! and to weakening and destruction of recrystallization texture. (tr-auth)
- Research Organization:
- Central Scientific Research Inst. of Ferrous Metallurgy, USSR
- NSA Number:
- NSA-14-014077
- OSTI ID:
- 4171308
- Journal Information:
- Fiz. Metal. i Metalloved., Journal Name: Fiz. Metal. i Metalloved. Vol. Vol: 8
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
DEFORMATION AND RECRYSTALLIZATION TEXTURES OF NICKEL AND OF ALLOYS ON NICKEL BASE
"SECONDARY" RECRYSTALLIZATION AND "TERTIARY" RECRYSTALLIZATION OF SOFT IRON COLD WORKED BY ROLLING AND ANNEALED UNDER HYDROGEN
PROGRESS REPORT NO. 9 ON ANNEALING OF COLD WORKED METALS
Journal Article
·
Fri Nov 30 23:00:00 EST 1962
· Z. Metallk.
·
OSTI ID:4734961
"SECONDARY" RECRYSTALLIZATION AND "TERTIARY" RECRYSTALLIZATION OF SOFT IRON COLD WORKED BY ROLLING AND ANNEALED UNDER HYDROGEN
Journal Article
·
Sun Feb 15 23:00:00 EST 1959
· Compt. rend.
·
OSTI ID:4271745
PROGRESS REPORT NO. 9 ON ANNEALING OF COLD WORKED METALS
Technical Report
·
Sat Oct 01 00:00:00 EDT 1960
·
OSTI ID:4037627