THE HOT PRESSING OF FINE GRAINED CERAMIC OXIDES FOR USE IN THERMAL CONDUCTIVITY STUDIES. Period covered: November 1, 1958 to October 31, 1959
Technical Report
·
OSTI ID:4137238
The relations between time, temperature, pressure, and grain growth in hot pressing were studied using alumina grain to determine the techniques neccesary for the production of dense polycrystalline alumina having a grain size in 4- io 5- mu range. It was found that alumina having a density of the order of 95% of theoretical and grain size in the desired range could be produced using a short time at maximum temperature n hot pressing. (auth)
- Research Organization:
- New York. State Univ. Coll. of Ceramics, Alfred
- NSA Number:
- NSA-15-001813
- OSTI ID:
- 4137238
- Report Number(s):
- WADC-TN-59-394; AD-236724
- Country of Publication:
- United States
- Language:
- English
Similar Records
GRAIN SIZE EFFECTS ON THE THERMAL CONDUCTIVITY OF CERAMIC OXIDES
GRAIN SIZE EFFECTS ON THE THERMAL CONDUCTIVITY OF CERAMIC OXIDES. Progress Report No. 9 for February 1, 1959 to April 30, 1959
GRAIN SIZE EFFECTS ON THE THERMAL CONDUCTIVITY OF CERAMIC OXIDES. Progress Report No. 11, November 1, 1959 to April 30, 1960
Technical Report
·
Tue Jan 31 23:00:00 EST 1961
·
OSTI ID:4039497
GRAIN SIZE EFFECTS ON THE THERMAL CONDUCTIVITY OF CERAMIC OXIDES. Progress Report No. 9 for February 1, 1959 to April 30, 1959
Technical Report
·
Sun Oct 30 23:00:00 EST 1960
·
OSTI ID:4189047
GRAIN SIZE EFFECTS ON THE THERMAL CONDUCTIVITY OF CERAMIC OXIDES. Progress Report No. 11, November 1, 1959 to April 30, 1960
Technical Report
·
Mon Oct 30 23:00:00 EST 1961
·
OSTI ID:4084500