SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Monthly Progress Report No. 9 for August 1 through August 31, 1960
Technical Report
·
OSTI ID:4124384
Several syuthesis experiments were carried out including production of a 3-lb batch of U/sub 3/Si/sub 2/ by the previously de scribed nonquenching method. Test data indicate that the use of graphite crucibles in syntheses increases the specimen carbon content. In other work, inconsistency between x-ray and metallographic-examination results of U/sub 3/Si/sub 2/ is being investigated. The fabrication of U/sub 3/Si/sub 2/ bars for physical testing was continued during the period. Synthesis of UN is reported in which pellet densities of 12.71 g/cm/sup 3/ (14.31 theoretical) were produced. Further sintering experiments on UC are also described, and data are given. (For preceding period see ORO-276.) (J.R.D.)
- Research Organization:
- Carborundum Co. Research and Development Div., Niagara Falls, N.Y.
- NSA Number:
- NSA-15-000540
- OSTI ID:
- 4124384
- Report Number(s):
- ORO-319
- Country of Publication:
- United States
- Language:
- English
Similar Records
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Quarterly Report No. 5, August 1 through October 31, 1960
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Monthly Progress Report No. 11, November 1-November 30, 1960
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Monthly Progress Report No. 7 for March 1 through March 31, 1960
Technical Report
·
Mon Nov 14 23:00:00 EST 1960
·
OSTI ID:4078369
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Monthly Progress Report No. 11, November 1-November 30, 1960
Technical Report
·
Mon Dec 12 23:00:00 EST 1960
·
OSTI ID:4059360
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Monthly Progress Report No. 7 for March 1 through March 31, 1960
Technical Report
·
Mon Apr 11 23:00:00 EST 1960
·
OSTI ID:4189558