SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Quarterly Report No. 5, August 1 through October 31, 1960
Additional quantities of UC, UN, and U/sub 3/Si/sup 2/ were prepared to be used in fabrication of test specimens for property determinations. A reduction in oxygen contamination of UN and U/sub 3/Si/sup 2/as achieved by improved techniques of synthesis.>s Preliminary values for thermal expansion, modulus of elasticity, and corrosion in boiling water were also obtained for these materials. (For preceding period see TID-6591.) (J.R.D.)
- Research Organization:
- Carborundum Co., Niagara Falls, N.Y.
- Sponsoring Organization:
- USDOE
- NSA Number:
- NSA-15-011544
- OSTI ID:
- 4078369
- Report Number(s):
- ORO-340
- Country of Publication:
- United States
- Language:
- English
Similar Records
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Monthly Progress Report No. 9 for August 1 through August 31, 1960
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Monthly Progress Report No. 11, November 1-November 30, 1960
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Summary Report for May 1959 through December 1960
Technical Report
·
Mon Sep 12 00:00:00 EDT 1960
·
OSTI ID:4124384
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Monthly Progress Report No. 11, November 1-November 30, 1960
Technical Report
·
Mon Dec 12 23:00:00 EST 1960
·
OSTI ID:4059360
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Summary Report for May 1959 through December 1960
Technical Report
·
Tue Jan 31 23:00:00 EST 1961
·
OSTI ID:4843747