EXTRUDING AND DRAWING MOLYBDENUM TO COMPLEX THIN H-SECTION. Interim Technical Engineering Report No, 2, October 1, 1963-December 31, 1963
Technical Report
·
OSTI ID:4110249
Sixteen solid round extrusions of TZM were made primarily to determine suitable die materials. Reduction ratios at 45: 1 and 55: 1 were accomplished from a billet temperature range of 3000 to 3500 deg F. On the basis of good surface quality and dimensional runout on round extrusions, H-shaped dies will be prepared with.035-inch flamesprayed zirconia as well as with pressed and sintered solid zirconia. Extrusion tooling performed well up to 237,000 psi liner pressure except for noticeable wear at the liner working surface. (auth)
- Research Organization:
- Allegheny Ludlum Steel Corp. Research Center, Brackenridge, Penna.
- NSA Number:
- NSA-18-012601
- OSTI ID:
- 4110249
- Report Number(s):
- RTD-TR-8-112
- Country of Publication:
- United States
- Language:
- English
Similar Records
LINER FOR EXTRUSION BILLET CONTAINERS. Interim Technical Documentary Progress Report, May 4-August 4, 1963
TUNGSTEN EXTRUSION DEVELOPMENT PROGRAM. Interim Technical Engineering Report, April 20, 1962-June 20, 1962
MOLYBDENUM ALLOY EXTRUSION DEVELOPMENT PROGRAM. Seventh Interim Technical Engineering and Phase III Report, June 1, 1962 to September 1, 1962
Technical Report
·
Fri Oct 30 23:00:00 EST 1964
·
OSTI ID:4034087
TUNGSTEN EXTRUSION DEVELOPMENT PROGRAM. Interim Technical Engineering Report, April 20, 1962-June 20, 1962
Technical Report
·
Tue Oct 30 23:00:00 EST 1962
·
OSTI ID:4789888
MOLYBDENUM ALLOY EXTRUSION DEVELOPMENT PROGRAM. Seventh Interim Technical Engineering and Phase III Report, June 1, 1962 to September 1, 1962
Technical Report
·
Sat Sep 01 00:00:00 EDT 1962
·
OSTI ID:4779377