THE EFFECTS OF RADIATION ON THE ELECTROCHEMICAL BEHAVIOR OF 1X18H9T STEEL

Journal Article · Wed Feb 01 04:00:00 EST 1961 · Atomnaya Energ.

OSTI ID:4058123

Gerasimov, V V; Aleksandrova, V N

A specially designed vitreous electrolytic cell, 20 mm in diameter and 400 mm high, was used in the investigation of radiation effects on the electrochemical behavior of lXl8H9T steel specimen (0.07 wt.% C; 1.23 wt.% Mn; 19.2 wt.% Cr; 10.5 wt.% Ni; and 0.53 wt.% Ti). The experiments were carried out wlth a cell placed in an active reactor zone with 10/sup 12/ neutrons/cm/sup 2/ - sec flux at 80 to 90 deg C. The irradiation did not affect the kinetics of the ancde prccess of lXl8H9T steel in O.OlN sodium sulfate. The polarization curves are plotted. (R.V.J.)

• Research Organization: Originating Research Org. not identified
• NSA Number: NSA-15-014812
• OSTI ID: 4058123
• Journal Information: Atomnaya Energ., Journal Name: Atomnaya Energ. Vol. Vol: 10
• Country of Publication: Country unknown/Code not available
• Language: Russian

Related Subjects

ANODES
CARBON
CHROMIUM
ELECTROCHEMISTRY
ELECTROLYTES
ELECTROLYTIC CELLS
IRRADIATION
MANGANESE
MATERIALS TESTING
METALS, CERAMICS, AND OTHER MATERIALS
NICKEL
POLARIZATION
QUANTITY RATIO
RADIATION EFFECTS
REACTORS
SODIUM SULFATES
SOLUTIONS
STEELS
TITANIUM