THE SOLUBILITIES OF Ni-Cr-Fe ALLOY 600 CORROSION PRODUCTS
Technical Report
·
OSTI ID:4030888
The solubilities of Ni--Cr--Fe Alloy 600 corrosion products formed at 550 deg F in ammoniated water, were determined as functions of time, temperature (75 to 650 deg F), and pH (8.5 to 10.5). Measurements were also made with pH- 10.0 lithiated water to determine the effect of another pH agent. The effects of oxygen concentration in solution and of preconditioning the Alloy 600 surface are also described. (auth)
- Research Organization:
- Knolls Atomic Power Lab., Schenectady, N.Y.
- DOE Contract Number:
- W-31-109-ENG-52
- NSA Number:
- NSA-18-018313
- OSTI ID:
- 4030888
- Report Number(s):
- KAPL-3017
- Country of Publication:
- United States
- Language:
- English
Similar Records
THE SOLUBILITY OF INCONEL CORROSION PRODUCTS
OUTLINE OF PWR ALTERNATE CONTROL MATERIAL INFORMATION OBTAINED AT BETTIS
SUSCEPTIBILITY OF AISI 410 TO STRESS CORROSION CRACKING IN HIGH TEMPERATURE, HIGH PURITY WATER
Technical Report
·
Mon Jan 29 23:00:00 EST 1962
·
OSTI ID:4795107
OUTLINE OF PWR ALTERNATE CONTROL MATERIAL INFORMATION OBTAINED AT BETTIS
Technical Report
·
Thu Aug 15 00:00:00 EDT 1957
·
OSTI ID:4306553
SUSCEPTIBILITY OF AISI 410 TO STRESS CORROSION CRACKING IN HIGH TEMPERATURE, HIGH PURITY WATER
Technical Report
·
Sun Feb 15 23:00:00 EST 1959
·
OSTI ID:4275003