STUDY OF COMBINATIONS OF HIGH AND LOW ELASTIC MODULUS CERAMIC MATERIALS. Quarterly Report No. 2, January 15, 1960-April 15, 1960
Technical Report
·
OSTI ID:4028488
Preliminary experiments to measure the modulus of elasticity as a function of temperature and composition by a sonic method indicate that accurate, consistent results can be obtained. The valus determined for ZrC was 48.8 x 104 psi. Modulus of rupture measurements was made for graphite and ZrC at 25 and 2000 deg C. (B.O.G.)
- Research Organization:
- Carborundum Co. Research and Development Div., Niagara Falls, N.Y.
- NSA Number:
- NSA-15-016057
- OSTI ID:
- 4028488
- Report Number(s):
- NP-9972
- Country of Publication:
- United States
- Language:
- English
Similar Records
STUDY OF COMBINATIONS OF HIGH AND LOW ELASTIC MODULUS CERAMIC MATERIALS. Quarterly Report No. 3, April 15, 1960-July 15, 1960
STUDY OF COMBINATIONS OF HIGH AND LOW ELASTIC MODULUS CERAMIC MATERIALS. Quarterly Report No. 5, March 15, 1960 through June 15, 1961
STUDY OF COMBINATIONS OF HIGH AND LOW ELASTIC MODULUS CERAMIC MATERIALS. Quarterly Report No. 4, December 15, 1960-March 15, 1961
Technical Report
·
Thu Jul 28 00:00:00 EDT 1960
·
OSTI ID:4032966
STUDY OF COMBINATIONS OF HIGH AND LOW ELASTIC MODULUS CERAMIC MATERIALS. Quarterly Report No. 5, March 15, 1960 through June 15, 1961
Technical Report
·
Thu Jun 15 00:00:00 EDT 1961
·
OSTI ID:4039170
STUDY OF COMBINATIONS OF HIGH AND LOW ELASTIC MODULUS CERAMIC MATERIALS. Quarterly Report No. 4, December 15, 1960-March 15, 1961
Technical Report
·
Thu Mar 16 23:00:00 EST 1961
·
OSTI ID:4028538