STUDY ON THE FABRICATION OF THE BeO-UO$sub 2$ SINTERED BODY BY MEANS OF VACUUM HOT PRESSING (in Japanese)
Journal Article
·
· J. Atomic Energy Soc. Japan
OSTI ID:4015002
BeO--UO/sub 2/ sintered bodies containing 2 to 10 wt% UO/sub 2/ were prepared in a graphite mold by hot pressing and induction heating for 60 min at 1,400 to 1,600 deg C under a compression of 160 kg/cm/sup 2/ in a vacuum of 10-/ sup 3/ mm Hg. Under the optimum pressing condition, bodies having the following properties are obtained: density up to 98% of theoretical; bending strength 1,900 to 2,300 kg/cm/sup 2/; thermal conductivity slightly decreased with UO/sub 2/ content down to 0.48 (at 10 wt% UO/sub 2/) cal/cm. sec. deg C at room temperature; linear expansion the same as BeO sintered bodies. (auth)
- Research Organization:
- Nippon Gaishi Kaisha, Ltd., Japan
- NSA Number:
- NSA-15-018473
- OSTI ID:
- 4015002
- Journal Information:
- J. Atomic Energy Soc. Japan, Journal Name: J. Atomic Energy Soc. Japan Vol. Vol: 3
- Country of Publication:
- Country unknown/Code not available
- Language:
- Japanese
Similar Records
Manufacture of UO$sub 2$- and UO$sub 2$-BeO Mixed Pellets. Final Report; HERSTELLUNG VON UO$sub 2$-UND UO$sub 2$-BeO-MISCHPELLETS
AN INVESTIGATION OF SOME PHYSICAL PROPERTIES OF SINTERED UO$sub 2$ BODIES AS A FUNCTION OF BeO ADDITIONS
SINTERABILITY STUDIES OF BeO COMPACTS
Technical Report
·
Mon Oct 01 00:00:00 EDT 1962
·
OSTI ID:4672992
AN INVESTIGATION OF SOME PHYSICAL PROPERTIES OF SINTERED UO$sub 2$ BODIES AS A FUNCTION OF BeO ADDITIONS
Journal Article
·
Thu Jan 31 23:00:00 EST 1963
· Ber. Deut. Keram. Ges.
·
OSTI ID:4690710
SINTERABILITY STUDIES OF BeO COMPACTS
Technical Report
·
Thu Jun 28 00:00:00 EDT 1962
·
OSTI ID:4775086