Inversion domains in GaN grown on sapphire
- Xerox Palo Alto Research Center, 3333 Coyote Hill Road, Palo Alto, California 94304 (United States)
- National Center of Electron Microscopy, Materials Science Division, Lawrence Berkeley Laboratory, University of California, Berkeley, California 94720 (United States)
Planar defects observed in GaN films grown on (0001) sapphire have been identified as inversion domain boundaries (IDBs) by a combination of high resolution transmission electron microscopy, multiple dark field imaging, and convergent beam electron diffraction techniques. Films grown by molecular beam epitaxy (MBE), metalorganic vapor deposition (MOCVD), and hydride vapor phase epitaxy (HVPE) were investigated and all were found to contain IDBs. The IDBs in the MBE and HVPE films extended from the interface to the film surface and formed columnar domains that ranged in width from 3 to 20 nm in the MBE films and up to 100 nm in the HVPE films. For the films investigated, the MBE films had the highest density, and the MOCVD films had the lowest density of IDBs. The nucleation of inversion domains (IDs) may result from step-related inhomogeneities of the GaN/sapphire interface. {copyright} {ital 1996 American Institute of Physics.}
- Research Organization:
- Lawrence Berkeley National Laboratory
- DOE Contract Number:
- AC03-76SF00098
- OSTI ID:
- 385633
- Journal Information:
- Applied Physics Letters, Journal Name: Applied Physics Letters Journal Issue: 16 Vol. 69; ISSN APPLAB; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hydride vapor phase homoepitaxial growth of GaN on MOCVD-grown templates[Metal Organic Chemical Vapor Deposition]
Inversion domains in AlN grown on (0001) sapphire