Study of nickel electrode oxidation as a function of 80% depth of discharge cycling
- Eagle-Picher Industries, Inc., Colorado Springs, CO (United States)
Oxidation of nickel sinter used in nickel oxide electrodes in aerospace nickel cadmium cells leads to hydrogen gassing and the potential for cell rupture. The oxidation is directly related to loss of overcharge protection built into the cell during manufacturing. In nickel hydrogen cells, excessive oxidation of the nickel sinter can eventually lead to a burst before leak situation and is a potential source of failure. It is well known that nickel cadmium cells having nylon separators contribute to loss of overcharge via a hydrolysis reaction of the nylon in the potassium hydroxide electrolyte environment in the cell. The hydrolysis reaction produces lower chain organics which are oxidized by the positive electrode and oxygen. Oxidation of the organics diminishes the overcharge protection. With introduction of the Super NiCd{trademark} and the Magnum{trademark} nickel cadmium cells the nylon hydrolysis reaction is eliminated, but any reducing agent in the cell such as nickel or an organic additive can contribute to loss of overcharge protection. The present effort describes chemical analyses made to evaluate the extent of overcharge protection loss in nickel cadmium cells which do not have nylon hydrolysis, and quantifies the amount of hydrogen buildup in nickel hydrogen cells which are subjected to 80% depth of discharge cycling with and without the presence of cadmium in the positive electrode.
- OSTI ID:
- 347752
- Report Number(s):
- CONF-970701--
- Country of Publication:
- United States
- Language:
- English
Similar Records
Performance evaluation of polypropylene and zirconia separators in sealed nickel-cadmium cells
Effects of cadmium-electrode properties on nickel-cadmium cell performance. Technical report