An organically templated layered vanadium oxide: Hydrothermal synthesis, single-crystal structure, and magnetic properties of (H{sub 3}N(CH{sub 2}){sub 3}NH{sub 3})[V{sub 4}O{sub 10}]
- NEC Research Inst., Princeton, NJ (United States)
The utilization of the hydrothermal technique in combination with cationic organic templates has been extensively used in the synthesis of zeolites and molecular sieves. Here, the authors report the hydrothermal synthesis and single-crystal structure of (H{sub 3}N(CH{sub 2}){sub 3}NH{sub 3})[V{sub 4}O{sub 10}], a layered mixed-valence vanadium oxide with organic ammonium cations between the layers. 21 refs., 4 figs.
- OSTI ID:
- 285002
- Journal Information:
- Chemistry of Materials, Journal Name: Chemistry of Materials Journal Issue: 3 Vol. 8; ISSN 0897-4756; ISSN CMATEX
- Country of Publication:
- United States
- Language:
- English
Similar Records
A novel organically templated three-dimensional open framework vanadium tellurite: (NH{sub 3}CH{sub 2}CH{sub 2}NH{sub 3}){sub 2}V{sub 2}Te{sub 6}O{sub 18}
Synthesis of new mixed valence compounds MV{sup 5+}V{sub 2}{sup 4+}O{sub 7}(M=NH{sub 4},K): Crystal structure of NH{sub 4}V{sub 3}O{sub 7} and electrical properties of KV{sub 3}O{sub 7}
Two new zincophosphates, (H{sub 3}NCH{sub 2}CH{sub 2}NH{sub 3}){sub 2}[Zn({mu}-PO{sub 4}){sub 2}] and (NH{sub 4})[(H{sub 3}N)Zn{l_brace}({mu}-PO{sub 4})Zn{r_brace}{sub 3}]: Crystal structures and relationships to similar open framework zinco- and aluminophospates
Journal Article
·
Wed Jun 15 00:00:00 EDT 2005
· Journal of Solid State Chemistry
·
OSTI ID:20725967
Synthesis of new mixed valence compounds MV{sup 5+}V{sub 2}{sup 4+}O{sub 7}(M=NH{sub 4},K): Crystal structure of NH{sub 4}V{sub 3}O{sub 7} and electrical properties of KV{sub 3}O{sub 7}
Journal Article
·
Sun Jul 15 00:00:00 EDT 2007
· Journal of Solid State Chemistry
·
OSTI ID:21015879
Two new zincophosphates, (H{sub 3}NCH{sub 2}CH{sub 2}NH{sub 3}){sub 2}[Zn({mu}-PO{sub 4}){sub 2}] and (NH{sub 4})[(H{sub 3}N)Zn{l_brace}({mu}-PO{sub 4})Zn{r_brace}{sub 3}]: Crystal structures and relationships to similar open framework zinco- and aluminophospates
Journal Article
·
Thu Sep 15 00:00:00 EDT 2011
· Journal of Solid State Chemistry
·
OSTI ID:21580270