Reactive ion etching-induced damage in AlAs/InGaAs heterostructure field-effect transistors processed in HBR plasma
Journal Article
·
· Journal of Vacuum Science and Technology. B, Microelectronics Processing and Phenomena
- Univ. of Illinois, Urbana, IL (United States); and others
An investigation of the effects of HBr reactive ion etching (RIE) processing for gate recessing in lattice-matched InAlAl/InGaAs heterostructure field-effect transitors (HFETs) has been conducted. The effect of varying the Schottky barrier layer thickness on device performance and the susceptibility of HFETs to RIE-induced damage are presented for barrier layer thicknesses ranging from 10 to 25 nm. The effect of plasma self-bias voltage during gate recess etching on overall device performance for a given layer is assessed through direct current (dc) characterization and transconductance, threshold voltage, reverse gate leakage current, and gate-drain breakdown voltage, and through microwave characterization of the devices. Devices with barrier layers less than 20 nm thick are found to suffer the most degradation due to the RIE-induced damage. For devices with sufficiently thick barrier layers, dc and microwave device parameters compare well with those of corresponding devices fabricated using a selective wet-etch process. 10 refs., 5 figs., 1 tab.
- OSTI ID:
- 263457
- Journal Information:
- Journal of Vacuum Science and Technology. B, Microelectronics Processing and Phenomena, Journal Name: Journal of Vacuum Science and Technology. B, Microelectronics Processing and Phenomena Journal Issue: 6 Vol. 12; ISSN JVTBD9; ISSN 0734-211X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Process technology for InGaAs/InAlAs modulation doped field effect transistors in InP substrates
Thermodynamically stable [ital p]-channel strained-layer AlGaAs/InGaAs/GaAs heterostructure field effect transistor
Surface- and sidewall-damage of InP-based optoelectronic devices during reactive ion etching using CH{sub 4}/H{sub 2}
Journal Article
·
Mon Oct 31 23:00:00 EST 1994
· Journal of Vacuum Science and Technology. B, Microelectronics Processing and Phenomena
·
OSTI ID:263458
Thermodynamically stable [ital p]-channel strained-layer AlGaAs/InGaAs/GaAs heterostructure field effect transistor
Journal Article
·
Mon Aug 08 00:00:00 EDT 1994
· Applied Physics Letters; (United States)
·
OSTI ID:7018774
Surface- and sidewall-damage of InP-based optoelectronic devices during reactive ion etching using CH{sub 4}/H{sub 2}
Book
·
Mon Dec 30 23:00:00 EST 1996
·
OSTI ID:536184