1300-nm gain obtained with dysprosium-doped chloride crystals
Conference
·
OSTI ID:247413
Dy{sup 3+} - doped chloride crystals have high 1300-nm emission quantum yields. Pump - probe experiments on La Cl{sub 3}:Dy{sup 3+} demonstrate optical gain consistent with predictions based on spectroscopic cross sections and lifetimes.
- Research Organization:
- Lawrence Livermore National Lab., CA (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 247413
- Report Number(s):
- UCRL-JC--123523; CONF-9607106--1; ON: DE96010835
- Country of Publication:
- United States
- Language:
- English
Similar Records
Spectroscopy and decay kinetics of Pr{sup 3+}-doped chloride crystals for 1300-nm optical amplifiers
Optical amplifier operating at 1.3 microns useful for telecommunications and based on dysprosium-doped metal chloride host materials
25 Gb s{sup −1} data transmission using a bismuth-doped fibre amplifier with a gain peak shifted to 1300 nm
Conference
·
Wed Mar 08 23:00:00 EST 1995
·
OSTI ID:83787
Optical amplifier operating at 1.3 microns useful for telecommunications and based on dysprosium-doped metal chloride host materials
Patent
·
Mon Dec 01 23:00:00 EST 1997
·
OSTI ID:563702
25 Gb s{sup −1} data transmission using a bismuth-doped fibre amplifier with a gain peak shifted to 1300 nm
Journal Article
·
Fri Nov 30 23:00:00 EST 2018
· Quantum Electronics (Woodbury, N.Y.)
·
OSTI ID:23004856