Metal oxide coatings for piezoelectric exhaust gas sensors
We have deposited ZrO{sub 2}, TiO{sub 2}, and SnO{sub 2} films on ST-cut quartz surface acoustic wave (SAW) devices via sol-gel techniques. The films range from 100 to 300 nm thick and have porosities after calcination at 300{degrees}C that range from 82-88 % for ZrO{sub 2}, 77-81% for TiO{sub 2}, and 57-66% for SnO{sub 2}. In all cases, we have varied the synthesis and processing parameters over a wide range to optimize film properties: metal ion concentration (0.05-1.0 M), the H{sub 2}O:metal ratio (0.3-5.3), the acid concentration in the sol (0.02-0.7 M), the modifier ligand:metal ratio (r = 0.0-1.0), the processing conditions (100-900{degrees}C). The modifier ligand, triethanolamine (TEA), is added to each solution to allow multilayer films to be made crack free. The multilayer films are studied by optical microscopy, ellipsometry, X-ray diffraction, and N{sub 2} sorption. Preliminary high temperature frequency response measurements to target gases, such as, H{sub 2}, NO, NO{sub 2}, and propylene indicate limited sensitivity for the configurations tested.
- Research Organization:
- Sandia National Labs., Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 244467
- Report Number(s):
- SAND--96-1178C; CONF-9606159--3; ON: DE96010551
- Country of Publication:
- United States
- Language:
- English
Similar Records
Corrosion resistance of ZrO{sub 2}–TiO{sub 2} nanocomposite multilayer thin films coated on carbon steel in hydrochloric acid solution
Development of a catalyst for conversion of syngas-derived materials to isobutylene. Technical progress report No. 6, July 1, 1992--September 30, 1992