Inhibition of Polyimide Photodegradation by Incorporation of Titanate Nanotubes into a Composite
- Institut Teknologi Bandung, Advanced Functional Materials (AFM) Laboratory, Engineering Physics (Indonesia)
- Research Centre for Nanosciences and Nanotechnology (RCNN), Institut Teknologi Bandung (Indonesia)
- University of Southampton, Energy Technology Research Group, Faculty of Engineering and the Physical Sciences (United Kingdom)
The effect of UV light exposure on the properties of hexafluoroisopropylidene-diphthalic anhydride–oxydianiline (6FDA–ODA) polyimide (PI) and polyimide–titanate nanotube (TiNT/PI) composites has been studied using Raman spectroscopy, optical microscopy, nanoidentation and TEM. The degree of polymer photodegradation was estimated by measuring the change in affinity to a positively charged dye (methylene blue, MB). The mechanism of photoassisted transformations in polyimides usually involves scission of polymer chains accompanied by appearance of active radicals, which undergo further rapid transformations to more stable phenol, amine, and carboxylic functional groups. The accumulation of these groups can increase the degree of adsorption of charged dyes in the photodegraded polymer. It was found that neat PI showed a significantly increased capacity to adsorb MB after irradiation with UV, reaching a plateau after 1 h. In contrast, TiNT/PI composite demonstrated a much slower rise in concentration of adsorbed MB even after 4 h of UV exposure. Raman spectra indicated cleavage of C=O and C–F bonds in PI while only the C–F bond was damaged in TiNT/PI. Shorter cracks (≈ 40 µm long) appeared in TiNT/PI composites whereas macro cracks (> 100 µm) were visible in neat PI after 3 h of UV exposure. Brittleness was studied by comparing plasticity index which varied from 0 to 1 (0 corresponding to the most brittle material and 1 the most ductile one). Plasticity index reduced by 51% and 2% for PI and TiNT/PI, respectively after 3 h UV irradiation, indicating that TiNT can protect underlying PI from further damage. The hardness of neat PI decreased whereas, for TiNT/PI, it increased under UV, suggesting crosslinking of broken polymer chains with nanotubes. Graphical Abstract: Photodegradation of a titanate nanotubes/polyimide composite can lead to cross-linking of broken polymer chains by nanostructured material, resulting in increased hardness. .
- OSTI ID:
- 22977109
- Journal Information:
- Journal of Polymers and the Environment, Vol. 27, Issue 7; Other Information: Copyright (c) 2019 Springer Science+Business Media, LLC, part of Springer Nature; Article Copyright (c) 2019 The Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 1566-2543
- Country of Publication:
- United States
- Language:
- English
Similar Records
Composite nanofibers for highly efficient photocatalytic degradation of organic dyes from contaminated water
Understanding the effects of backbone chemistry and anion type on the structure and thermal behaviors of imidazolium polyimide‐ionenes