Radiation-induced swelling and radiation-induced segregation & precipitation in dual beam irradiated Ferritic/Martensitic HT9 steel
Highlights: • The depth-dependence of radiation-induced cavities was characterized in self-ion irradiated HT9 co-implanted with He. • The injected interstitial effect was revealed to suppress cavity swelling in the vicinity of the damage peak. • ChemiSTEM elemental maps revealed the segregation of Ni at cavity surfaces and its possible synergistic influence on swelling was discussed. - Abstract: Ferritic/Martensitic HT9 steel was irradiated at 432 °C to 16.6 displacements per atom (dpa) (at the depth of 600 nm) using a defocused beam of 5 MeV Fe{sup ++} ions, while co-implanted with 3.22 appm He at the same depth. The helium concentration profile was designed so to follow the damage curve with a 0.22 appm He/dpa ratio at the depth from 300 to 1000 nm in the material. The depth-dependence of the cavity size and number density were characterized by both transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM) imaging methods. A comparison between the two techniques was done showing good agreement. Cavity number density and the resulting swelling were found to be suppressed by the injected interstitial effect in the vicinity of the ion induced damage peak. The region between 300 and 750 nm depth which excludes the injected interstitial effect was thus proposed for improved cavity swelling analysis. The swelling ratio in this region was found to be ~(0.86–1.02) × 10{sup − 2}%/dpa. In addition, ChemiSTEM characterization revealed radiation-induced segregation occurring throughout the irradiated region and precipitation of G-phase particles. Segregation of Ni to cavity surfaces was also observed and its possible synergistic influence on swelling was discussed.
- OSTI ID:
- 22804818
- Journal Information:
- Materials Characterization, Vol. 134; Other Information: Copyright (c) 2017 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
Radiation induced segregation and precipitation behavior in self-ion irradiated Ferritic/Martensitic HT9 steel
The effect of helium on cavity swelling in dual-ion irradiated Fe and Fe-10Cr ferritic alloys