Effect of boron on the structural and magnetic properties of Co{sub 2}FeSi{sub 1-x}B{sub x} Heusler alloys
Journal Article
·
· AIP Conference Proceedings
- Defence Metallurgical Research Laboratory (DMRL), Kanchanbagh, Hyderabad – 500058 (India)
The partial substitution of Si with B on the structural and magnetic properties of Co{sub 2}FeSi{sub 1-x}Bx (x = 0-0.5) alloys was systematically investigated. X-ray and microstructural investigations show the presence of second phase at the grain boundaries which increases with increasing boron content. From thermal analysis studies, it was observed that L2{sub 1}-B2 ordering temperature remain constant whereas the melting point decreases with increase in boron addition and merges with ordering temperature at x = 0.5. The increase in T{sub C} for the alloys x ≥ 0.25 was attributed to the increase in second phase due to boron.
- OSTI ID:
- 22608842
- Journal Information:
- AIP Conference Proceedings, Vol. 1731, Issue 1; Conference: DAE solid state physics symposium 2015, Uttar Pradesh (India), 21-25 Dec 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural, magnetic, and transport properties of full-Heusler alloy Co{sub 2}(Cr{sub 1-x}Fe{sub x})Al thin films
Disorder-induced reversal of spin polarization in the Heusler alloy Co{sub 2}FeSi
Improvement of magnetic and structural stabilities in high-quality Co{sub 2}FeSi{sub 1−x}Al{sub x}/Si heterointerfaces
Journal Article
·
Wed Dec 01 00:00:00 EST 2004
· Journal of Applied Physics
·
OSTI ID:22608842
+2 more
Disorder-induced reversal of spin polarization in the Heusler alloy Co{sub 2}FeSi
Journal Article
·
Fri Apr 01 00:00:00 EDT 2011
· Physical Review. B, Condensed Matter and Materials Physics
·
OSTI ID:22608842
+5 more
Improvement of magnetic and structural stabilities in high-quality Co{sub 2}FeSi{sub 1−x}Al{sub x}/Si heterointerfaces
Journal Article
·
Mon Aug 18 00:00:00 EDT 2014
· Applied Physics Letters
·
OSTI ID:22608842
+2 more