Synthesis and characterization of indium doped La{sub 3}Co{sub 4}Sn{sub 13} skutterudite superconductor
- School of Physical sciences, Jawaharlal Nehru University, New Delhi-110067 (India)
We report the synthesis and characterization of a novel superconductor La{sub 3}Co{sub 4}Sn{sub 12.35}In{sub 0.65} by Indium doping at Tin site in parent compound La{sub 3}Co{sub 4}Sn{sub 13}. We observe enhanced T{sub c} along with improved superconducting properties as onset compared to parent compound. By transport measurements we get superconducting transition with T{sub c}{sup onset} = 4.7 K and T{sub c}{sup zero} = 3.2 K. In magnetization measurements (ZFC-FC) superconducting transition is observed at 5.1 K. Upper critical field (H{sub c2}) and lower critical field (H{sub c1}) calculated by magneto resistance and M-H loop measurement are found to be 1.65 T and 0.0026 T respectively. Hall measurement shows the majority charge carrier as electrons with carrier density of the order of 10{sup 19} cm{sup −3}. TEP measurement also support the Hall data as the Seebeck coefficient is negative over whole temperature range of measurement.
- OSTI ID:
- 22606544
- Journal Information:
- AIP Conference Proceedings, Vol. 1728, Issue 1; Conference: ICC 2015: International conference on condensed matter and applied physics, Bikaner (India), 30-31 Oct 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Superconducting and magneto-transport properties of BiS{sub 2} based superconductor PrO{sub 1-x}F{sub x}BiS{sub 2} (x = 0 to 0.9)
New oxypnictide superconductors: PrOFe{sub 1-x}Co{sub x}As
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
CARRIER DENSITY
CHARGE CARRIERS
COBALT COMPOUNDS
COMPARATIVE EVALUATIONS
CRITICAL FIELD
DOPED MATERIALS
INDIUM ADDITIONS
LANTHANUM COMPOUNDS
MAGNETIZATION
MAGNETORESISTANCE
SUPERCONDUCTORS
SYNTHESIS
TEMPERATURE RANGE 0000-0013 K
TIN COMPOUNDS
TRANSITION TEMPERATURE