Effect of SMAT on microstructural and mechanical properties of AA2024
In recent days surface mechanical attrition treatment (SMAT) had attracted the attention of researchers as it produces a nano-crystalline surface with improved mechanical properties. In the present study Al-4%Cu alloy used in automobile and aerospace application is subjected to surface mechanical attrition treatment using steel shots. The microstructural changes introduced on the surface of the Al alloy was investigated using Scanning Electron Microscopy (SEM). The secondary phases formed during the SMAT process is been investigated using EDX and XRD analysis. The effects of SMAT on the mechanical properties were analyzed using a tensile testing. The SMA treatment had resulted in severe plastic deformation of the surface, thereby yielded a nanocrystalline surface with a grain size of 30 to 50 nm. Further, it is also found that the SMAT produced ultra nanocrystalline particles of Cu{sub 2}Al dispersed uniformly into α-Al matrix. These microstructural changes had resulted in considerable change in the mechanical properties of these alloys. The tensile strength of these alloys had increased from ∼212 MPa to 303 MPa while the fracture toughness increased up to 28% in 10 minutes of SMAT.
- OSTI ID:
- 22606415
- Journal Information:
- AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 1728; ISSN 0094-243X; ISSN APCPCS
- Country of Publication:
- United States
- Language:
- English
Similar Records
In-depth quantitative analysis of the microstructures produced by Surface Mechanical Attrition Treatment (SMAT)
Microstructure detection of Mg-Zi-Ti-Si amorphous composite coating prepared by SMAT
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ALUMINIUM ALLOYS
COPPER ALLOYS
CRYSTALS
ELECTRON SCANNING
FRACTURE PROPERTIES
FRACTURES
GRAIN SIZE
NANOSTRUCTURES
PLASTICITY
PLASTICS
PRESSURE RANGE MEGA PA
SCANNING ELECTRON MICROSCOPY
STEELS
SURFACE TREATMENTS
SURFACES
TENSILE PROPERTIES
TESTING
THERMOMECHANICAL TREATMENTS
X-RAY DIFFRACTION
X-RAY SPECTROSCOPY